A thin-film gold conductor for an integrated circuit in a satellite application is deposited from a vapor, and the deposited gol
d thin film has a high resistivity. It is proposed that the high resistivity is due to a high non-equilibrium vacancy concentration, created when the vapor atoms rapidly condense into the thin film. To reduce the vacancy concentration, it is proposed to anneal (heat) the gold to a temperature that will result in only 1 vacancy for every 108 gold atoms, and then to cool the film slowly to room temperature. The enthalpy of formation for 1 vacancy in gold is equal to 0.94 eV. Specify the temperature
1 answer:
Answer:
Explanation:
Considering the relation of the equilibrium vacancy concentration ;
nv/N = exp (-ΔHv/KT)
Where T is the temperature at which the vacancy sites are formed
K = Boltzmaan constant
ΔHv = enthalpy of vacancy formation
Rearranging the equation and expressing in term of the temperature and plugging the values given to get the temperature. The detailed steps is as shown in the attached file
You might be interested in
Answer:
The long derivation for work of a mechanically reversible, isothermal compression was done with detailed steps as shown in the attachment.
Explanation:
what is applied here is a long derivation from Work done in an isobaric process, the expression for the compressibility factor (Z) and the equation of state that was given. The requisite knowledge of Differentiation and Integration was used.
The detailed derivation from firs principle is as shown in the attachment.
Answer:
The preliminary work breakdown structure will be divided into two steps, the first is to draw the first level and the second is to draw the second level.
Explanation:
Please look at attachment.